AGS e manino mai le 0.50 i le 13.2 µm.E ui lava o lona nonlinear opitika coefficient o le aupito maualalo i totonu o tioata infrared taʻua, maualuga puʻupuʻu galu manino manino edging i le 550 nm o loʻo faʻaaogaina i OPOs pamu e Nd: YAG laser;i le tele o eseesega fa'afefiloi fa'ata'ita'iga fa'atasi ma le diode, Ti:Safaira, Nd:YAG ma IR fa'alanu leisa e ufiufi ai le 3-12 µm;i faiga fa'asagatonu infrared, ma mo le SHG o le CO2 laser.O ipu tioata manifinifi AgGaS2 (AGS) e ta'uta'ua mo le fa'atupuina o pusi pu'upu'u i totonu ole vaeluagalemu ole IR e ala ile eseesega ole fa'atuputeleina ole fa'aogaina ole pulusi ole umi ole NIR.

Lattice tapula'a:a = 5.757, c = 10.311 Å

Lisi Lisi:997 °C

Malosi:4.702 g/cm3

Malosi o Mohs:3-3.5

Fa'ai'uga fa'asa'o:0.6 cm-1 @ 10.6 µm

Feso'ota'iga Dielectric tumau @ 25:ε11s=10ε11t=14

WhatsApp Auina imeli ia matou La'u mai ile PDF

Fa'amatalaga Oloa

Vaega Fa'atekinisi

Lipoti o Su'ega

Lisi o oloa

Talosaga:

• Fa'atupu fa'atasiga lona lua ile CO ma CO2 - lasers
• Optical parametric oscilator
• Eseese fa'atupu fa'avevesi i le ogatotonu o le infrared itulagi e o'o atu i le 12μm.
• Fa'afefiloi taimi i le ogatotonu IR itulagi mai le 4.0 i le 18.3 µm
• Tuneable lesi setete malo (OPO pamu e Nd:YAG ma isi lasers faagaoioia i le 1200 i le 10000 nm itulagi ma le lelei 0.1 i 10%)
• Fa'amama vaapiapi mata i le itulagi e lata ane i le isotropic point (0.4974 m i le 300 °K), fa'apipi'i fa'aili i le fesuiaiga o le vevela
• Suiga i luga o le CO2 leisa leisa ata i le latalata-IR po'o le va'aia itulagi e ala i le fa'aogaina/po'o le fa'aogaina o le Nd:YAG, ruby po'o le vali leisa ma le lelei e o'o atu i le 30%

Meatotino Autu
Lattice tapula'a	a = 5.757, c = 10.311 Å
Ole fa'asologa ole laina ile 10.6 um	d36 = 12.5 pm/V
Fa'ailoga fa'aleagaina o mata i le 10.6 um, 150 ns	10 - 20 MW/cm2
tutusa i le itu-c	12.5 x 10-6 x °C-1
fa'atutusa i le c-axis	-13.2 x 10-6 x °C-1
Fauga tioata	Tetragonal
Cell Parameters	a=5.756 Å, c=10.301 Å
Lisi Lisi	997 °C
Malosi	4.702 g/cm3
Mohs Malosi	3-3.5
Fa'asa'o Fa'asa'o	0.6 cm-1 @ 10.6 µm
Fa'atasi le Dielectric tumau @ 25 MHz	ε11s=10ε11t=14
Coefficient Fa'alauteleina o le vevela	\|\|C: -13.2 x 10-6 /oC⊥C: +12.5 x 10-6 /oC
Amioga vevela	1.5 W/M/°C

Vaega Fa'atekinisi
Fa'aletonu i luma galu	itiiti ifo i le λ/6 @ 633 nm
Fa'apalepale fua	(W +/-0.1 mm) x (H +/-0.1 mm) x (L +0.2 mm/-0.1 mm)
manino avanoa	> 90% nofoaga tutotonu
Mafolafola	λ/6 @ 633 nm mo T>=1.0mm
Tulaga lelei	Su'e/eli 20/10 ile MIL-O-13830A
Fa'atusa	sili atu nai lo le 1 arc min
Fa'asa'o	5 arc minute
Fa'apalepale tulimanu	Δθ < +/-0.25o, Δφ < +/-0.25o

Fa'ata'ita'iga	Oloa	Tele	Fa'atonuga	Laufanua	Mauga	Tele
DE0742-1	AGS	550.4mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	6
DE0053	AGS	550.5mm	θ=41.3°φ=0°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	1
DE0741	AGS	551mm	θ=39°φ=45°	Ua polesi itu uma e lua	Le fa'amauina	1
DE0743	AGS	662mm	θ=54.9°φ=45°	Ua polesi itu uma e lua	Le fa'amauina	1
DE0891-1	AGS	662mm	θ=50°φ=0°	Ua polesi itu uma e lua	Le fa'amauina	3
DE0149	AGS	880.38mm	θ=41.6°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	1
DE0367	AGS	880.4mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ25.4mm	1
DE0367-0	AGS	880.4mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	8
DE0367-1	AGS	880.4mm	θ=37°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	8
DE0367-2	AGS	880.4mm	θ=37°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ25.4mm	1
DE0367-3	AGS	880.4mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ25.4mm	1
DE0119	AGS	881mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ25.4mm	3
DE0119-0	AGS	881mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ15.4mm	3
DE0119-1	AGS	881mm	θ=37°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	7
DE0119-3	AGS	881mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	Le fa'amauina	5
DE0671	AGS	881mm	θ=39°φ=45°	Ua polesi itu uma e lua	Le fa'amauina	1
DE0957	AGS	φ3*0.4mm	θ=39°φ=45°	AR/AR@1.1-2.6μm+2.6-12μm	φ25.4mm	1